%0 Journal Article %T The Effect of Silica Particles Derived from Rice Husk on Some Mechanical Properties of a High Impact Heat Cure Acrylic Resin %J Journal of Medicinal and Chemical Sciences %I Sami Publishing Company (SPC) %Z 2651-4702 %A Khairi, Azza Walaaldeen %A Abdul-Hamid Naji, Ghassan %D 2023 %\ 07/01/2023 %V 6 %N 7 %P 1646-1659 %! The Effect of Silica Particles Derived from Rice Husk on Some Mechanical Properties of a High Impact Heat Cure Acrylic Resin %K High impact acrylic resin %K Silica %K Nanofiller %R 10.26655/JMCHEMSCI.2023.7.15 %X Background: Despite the fact that the mechanical properties of PMMA appliances and goods are not ideal, the goal of this research was to reinforce high impact acrylic dentures with rice husk-derived silica in various concentrations to improve some of the mechanical qualities of the denture base.Materials and Method: Based on the pilot study made in College of Dentistry University of Baghdad, to create the specimens, silica particles from a rice husk source were added to high impact heat cure resin at 1 wt.% and 3 wt.% (by weight). On the basis of the three tests conducted the transverse strength, impact strength and hardness tests, the prepared samples were evaluated using Fourier-transform infrared spectroscopy (FT-IR), particle size analysis, and a field emission scanning electron microscope (FE-SEM).Results: The results revealed that the addition of silica particles yielded a significantly improvement in transverse strength test (P-value= 0.001), and non-significantly increase in both impact strength and hardness values compared with the control group.Conclusion: Silica particles prepared from natural resource waste was successfully added into the high impact acrylic resin. It seemed that adding 1 wt.% and 3 wt.% silica particles. The most beneficial effects were obtained by improving the mechanical properties of high impact acrylic dentures. %U https://www.jmchemsci.com/article_162063_53f1a868f00a34c7e84ac8f19ebb9e2e.pdf